PET无胶单-双面系列
产品简介 Products Introduction
|
PET无胶单/双面板 |
|||||||||
| 产品主要特性 | |||||||||
|
1.极佳的挠曲性及剥离强度 2.耐温性达到260℃ 3.优异的电性能和绝缘性 4.优异的尺寸安定性 5.无卤，阻燃达到UL94-0 |
1.Outstanding flexibility and peel strength 2.Excellent thermal resistance 3.Excellent electrical performance and insulation performance 4.Excellent dimensional stability 5.Halogen free,and UL94V-0 |
||||||||
| 产品结构搭配 | |||||||||
|
|||||||||
PET无胶双面产品性能表（Performance Intrduction）
|
NO. |
Test Item 检验项目 |
Property 产品性能 |
Test Method 测试方法 |
||
|
1 |
Product mix 产品结构 |
|
/ |
||
|
2 |
Product mix 产品搭配 |
12 ED |
PET100 |
/ |
|
|
3 |
Thickness 厚度 |
125 |
IPC-TM-650 Method 2.11.1 |
||
|
4 |
Peel Strength 剥离强度（Kgf/cm） |
90°剥离 |
＞0.7 |
IPC-TM-650 Method 2.4.9 |
|
|
5 |
Dimensional Stability 收缩率（%） |
Method B |
±0.15 |
IPC-TM-650 Method 2.2.4 |
|
|
Method C |
±0.15 |
||||
|
7 |
Chemical Resistance 耐化性(Drop %) |
＜6 |
IPC-TM-650 Method 2.3.2 |
||
|
8 |
Solder Float Resistance 耐焊 |
OK |
IPC-TM-650 Method 2.4.13 |
||
|
9 |
Etched appearance 全蚀刻外观 |
OK |
TAIFLEX Method |
||
|
10 |
Dielectric Congstant(1GHZ) 介电常数 |
2.1 |
IPC-TM-650 Method 2.5.5 |
||
|
11 |
Tg(℃) |
260 |
DMA |
||
|
12 |
CTE(ppm/ ℃) |
33 |
DMA |
||
|
13 |
UL Flammability |
VTM-0 |
UL |
||
|
14 |
Moisture Absorption吸⽔率 |
0.2 |
Kaneka method |
||
产品简介 Products Introduction
|
PET无胶单/双面板 |
|||||||||
| 产品主要特性 | |||||||||
|
1.极佳的挠曲性及剥离强度 2.耐温性达到260℃ 3.优异的电性能和绝缘性 4.优异的尺寸安定性 5.无卤，阻燃达到UL94-0 |
1.Outstanding flexibility and peel strength 2.Excellent thermal resistance 3.Excellent electrical performance and insulation performance 4.Excellent dimensional stability 5.Halogen free,and UL94V-0 |
||||||||
| 产品结构搭配 | |||||||||
|
|||||||||
PET无胶双面产品性能表（Performance Intrduction）
|
NO. |
Test Item 检验项目 |
Property 产品性能 |
Test Method 测试方法 |
||
|
1 |
Product mix 产品结构 |
|
/ |
||
|
2 |
Product mix 产品搭配 |
12 ED |
PET100 |
/ |
|
|
3 |
Thickness 厚度 |
125 |
IPC-TM-650 Method 2.11.1 |
||
|
4 |
Peel Strength 剥离强度（Kgf/cm） |
90°剥离 |
＞0.7 |
IPC-TM-650 Method 2.4.9 |
|
|
5 |
Dimensional Stability 收缩率（%） |
Method B |
±0.15 |
IPC-TM-650 Method 2.2.4 |
|
|
Method C |
±0.15 |
||||
|
7 |
Chemical Resistance 耐化性(Drop %) |
＜6 |
IPC-TM-650 Method 2.3.2 |
||
|
8 |
Solder Float Resistance 耐焊 |
OK |
IPC-TM-650 Method 2.4.13 |
||
|
9 |
Etched appearance 全蚀刻外观 |
OK |
TAIFLEX Method |
||
|
10 |
Dielectric Congstant(1GHZ) 介电常数 |
2.1 |
IPC-TM-650 Method 2.5.5 |
||
|
11 |
Tg(℃) |
260 |
DMA |
||
|
12 |
CTE(ppm/ ℃) |
33 |
DMA |
||
|
13 |
UL Flammability |
VTM-0 |
UL |
||
|
14 |
Moisture Absorption吸⽔率 |
0.2 |
Kaneka method |
||